Inorganic compounds

ABSTRACT

The invention relates to a chemical compound of the formula Ni b M1 c M2 d (O) x (OH) y , wherein M1 denotes at least one element from the group consisting of Fe, Co, Mg, Zn, Cu and/or mixtures thereof, M2 denotes at least one element from the group consisting of Mn, Al, B, Ca, Cr and/or mixtures thereof, wherein b≦0.8, c≦0.5, d≦0.5, and x is a number between 0.1 and 0.8, y is a number between 1.2 and 1.9, and x+y=2. A process for the preparation thereof, and the use thereof as a precursor for the preparation of cathode material for secondary lithium batteries are described.

This application is a divisional of application Ser. No. 11/990,273 filed Mar. 10, 2009 which in turn is a U.S. national phase of International Application No. PCT/EP2006/007816 filed 8 Aug. 2006 which designated the U.S. and claims priority to DE 10 2005 038 158.8 filed 12 Aug. 2005, the entire contents of each of which are hereby incorporated by reference.

The present invention relates to a chemical compound of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y), a process for the preparation thereof and the use thereof as a precursor for the preparation of cathode material for lithium secondary batteries.

BACKGROUND OF THE INVENTION

Portable and cordless electrical equipment is widely used. Due to the ever more progressive miniaturization of this portable electronic equipment, the demand for ever smaller and more lightweight secondary batteries of high energy density, which serve as the energy source for such equipment, has risen at lightning speed in recent years. Lithium secondary batteries with non-aqueous electrolyte liquids have the desired properties.

This type of secondary batteries is distinguished by a positive electrode, the active material of which can reversibly embed and release lithium ions.

Composite oxides which in each case comprise lithium and at least one transition metal are known as suitable active substances for the positive electrodes of such secondary batteries. Examples are LiCoO₂, LiNiO₂ or also LiNi_(0.8)Co_(0.2)O₂. However, these material have various disadvantages. LiCoO₂, which is currently still used most frequently in lithium secondary batteries, has the disadvantage of a very high price of cobalt. Nickel is indeed less expensive than cobalt, but the high nickel-containing active masses have the disadvantage that when they are employed in secondary batteries they have the effect of an inadequate heat stability of the battery.

Among the materials mentioned, there was still no active substance for lithium secondary batteries for which the charging/discharging capacity, the resistance in the course of the electrochemical cycles, the thermal reliability and the cost aspect were simultaneously satisfactory.

JP 10-27611 proposes employing an at least bimetallic mixed hydroxide as a precursor for the synthesis of the lithium mixed metal oxide to improve the electrochemical properties. In addition to the elements nickel and cobalt, the elements aluminium and manganese, inter alia, are also mentioned in this context as a third metallic component for co-precipitation of the mixed metal hydroxide. It is recommended that the amount of doping elements (metallic components with the exception of nickel) is 10-30 mol % of the total amount of metal. At an amount of these metallic doping components of less than 10 mol %, a battery with this active mass has an inadequate cycle stability, while at an amount of greater than 30 mol %, the spherical particle shape is difficult to maintain in the precursor.

US 2002/0053663 A1 and US 2003/0059490 A1 propose composite oxides which comprise lithium, nickel, cobalt and manganese. In this context, co-precipitated mixed hydroxides of nickel, cobalt and manganese form the starting substance for the later mixed oxides. Both the electrochemical charging/discharging properties of the secondary battery and the high temperature stability are said to be improved by the doping elements cobalt and manganese in the lithium mixed metal oxide. In order to achieve these aims, higher concentrations of cobalt and manganese are required compared with the compounds mentioned in JP 10-27611. The upper limit mentioned for cobalt and manganese in US 2002/0053663 A1 is in each case 33 mol %, based on the total amount of the metallic transition elements.

According to US 2002/0053663 A1, to date it has been very difficult to prepare a suitable precursor for the mixed metal oxides. In particular, co-precipitation of a mixed metal hydroxide comprising the elements nickel, cobalt and manganese which would meet requirements in respect of the tap density of the powder has not been successful. In the case of the mixed metal oxides, it is very important that they are distinguished by a high tap density, because the high tap density leads to an increase in the volumetric energy density of the battery. In this context, the tap density of the co-precipitated mixed metal hydroxide has a direct influence on the later tap density of the lithium mixed metal oxide. In US 2002/0053663 A1, mixed hydroxides comprising nickel, cobalt and manganese and having a high tap density of 1.5 g/cm³ or higher are successfully synthesized either by the precipitation process of the mixed hydroxides taking place in an inert gas atmosphere or by a reducing agent being present in the product suspension. It is assumed that by vigorous stirring during the precipitation reaction, a partial oxidation of the elements Co(II) and manganese(II) takes place by inclusion of air, which leads to a reduction in the tap density for the co-precipitated mixed hydroxide. In US 2002/0053663 A1, a high stirring speed is recommended, which leads to an abrasion mechanism between the particles. The interaction between abrasion and particle growth is said to be a guarantee for production of spherical particles. It is therefore obvious that the desired abrasion leads to a limitation of the average particle sizes of the secondary particles.

US 2003/0054251 A1 describes an optimized process route for the synthesis of nickel- and manganese-containing mixed oxides as an active mass for lithium secondary batteries. The main aim of this invention is to heat-treat the co-precipitated mixed hydroxides (e.g. comprising Ni, Co, Mn) at 300-500° C. before the actual oven process. i.e. before the conversion into the lithium mixed metal oxide, in order to obtain the so-called dry precursor. A lithium component is then added to this dry precursor and the mixture is converted into the mixed metal oxide by calcining. If the dried precursor described is employed instead of a non-dried mixed hydroxide, according to US 2003/0054251 A1 an end product is obtained which is distinguished by a higher consistency of the product than in the case of materials for which the non-dried mixed hydroxide is employed. The consistency of the product from the materials was determined by producing in each case twenty batteries with each material and evaluating the variation of the decrease in capacity between the third and three-hundredth electrochemical cycle for these twenty batteries.

However, the additional thermal step of “precursor drying” and the stated use of lithium hydroxide instead of the less expensive lithium carbonate make the process both complicated and expensive.

WO 2004/092073 A1 also relates to mixed metal precursors for the synthesis of lithium mixed metal oxide. As in US 2003/0054251 A1, an ideal precursor for the synthesis of this compound class is sought here. In this context, US 2003/0054251 A1 is mentioned, inter alia, as prior art. Since the heat treatment of the precursor, as described in US 2003/0054251, is very involved and the subsequent use of LiOH is very expensive compared with Li₂CO₃, an oxidation of the co-precipitated N—Co—Mn hydroxide to give an N—Co—Mn oxyhydroxide is proposed as an alternative here.

The oxidation is carried out using an oxidizing agent such as dissolved air, sodium hypochlorite, hydrogen peroxide solution, potassium peroxodisulfate or bromine.

In the examples given it is striking that a very involved process is likewise employed. After the co-precipitation of the nickel-cobalt-manganese hydroxide, a filtration is first carried out, and then a washing of the residue on the filter in order to obtain a purified mixed metal hydroxide. Thereafter, the metal hydroxide is suspended again in an aqueous solution which contains the oxidizing agent and is oxidized over a certain period of time at a particular temperature to give a nickel-cobalt-manganese oxyhydroxide.

Thereafter, a filtration and a washing of the product obtained are again carried out.

It can be assumed that the first washing is carried out because during the subsequent oxidation of the mixed hydroxide there is the risk that in addition to a beta-NiOOH phase, a gamma-NiOOH phase also additionally forms. This phase has a significant expansion in volume compared with the beta-NiOOH phase because of an interlaminar expansion, which facilitates embedding of foreign ions, such as e.g. Na⁺ etc. The interlaminar expansion is already known from J. Power Sources, 8 (1982), 229. Only by a washing of the mixed hydroxide, as is proposed in WO 2004/092073A1, and subsequent suspending in an aqueous phase having a low concentration of foreign ions, can a significant incorporation of foreign ions into the crystal lattice structure be avoided. The foreign ions, such as Na⁺, are not dissolved out of the crystal lattice structure again during further conversion of the mixed metal hydroxide into the lithium mixed metal oxide, and are thus an impurity in the end product. When incorporated into the later lithium layers, in particular, the Na⁺ impurity can significantly impede diffusion of the lithium and therefore significantly impair the behaviour of the material in the battery.

Since the average valency of the metals in Example 1 of WO 2004/092073 A1 is stated as 2.97, and since it is known that Mn²⁺ is considerably easier to oxidize than Ni²⁺, it is to be assumed that the Mn has been partly oxidized to a valency of four and thus leads to the local formation of non-stoichiometric gamma-NiOOH.

US 2002/0053663 A1 discloses co-precipitated nickel-cobalt-manganese hydroxides, emphasis being placed on being able to synthesize a co-precipitated nickel-cobalt-manganese hydroxide having a high tap density. The hydroxide serves as a precursor for the lithium mixed metal oxides, which in turn is employed as an active mass in lithium secondary batteries. The tap density of the lithium mixed metal oxide is in turn of great importance and is influenced quite considerably by the tap density of the precursor. Alongside the tap density, however, further important parameters of the mixed hydroxide as a precursor for lithium mixed metal oxides are not dealt with.

US 2003/0054251 A1 explicitly points out that it is advantageous to use lithium hydroxide as the Li component, since the particle shape and the crystallinity can be controlled better with this Li component compared with lithium carbonate.

In WO 2004/092073 A1 the consequence is drawn from the above problems and the mixed hydroxide serving as a precursor in the prior art is oxidized to an oxyhydroxide before it is employed as a precursor for the synthesis of a lithium mixed metal oxide. In this context, however, a very involved synthesis route is taken, which according to the examples given comprises both two filtrations and two washings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing an X-ray diffraction spectrum of a partly oxidized mixed metal hydroxide according to the invention;

FIG. 2 is a SEM photograph showing particular sphericity and compactness;

FIGS. 3 and 4 are SEM photographs of the end product;

FIG. 5 is an X-ray diffraction spectrum of a synthesized compound;

FIGS. 6 and 7 are SEM photographs of an end product;

FIG. 8 is a graph showing the electrochemical performance of the product of Example 1 and Comparison Example 1,

FIG. 9 is an XDA spectrum, and

FIG. 10 is another XDA spectrum showing a gamma phase.

BRIEF DESCRIPTION OF THE INVENTION

The object of the present invention is therefore to provide a mixed metal compound, as a precursor for the preparation of cathode material for lithium secondary batteries, which contains no gamma-oxyhydroxide structures and/or alpha-hydroxide structures, is distinguished by a high tap density, has low sodium contents and allows the synthesis of a high-quality lithium mixed metal compound. The object of the present invention is furthermore to provide a economical process for the preparation of partly oxidized mixed metal hydroxides.

The object is achieved by a chemical compound of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y)

-   -   wherein     -   M1 denotes at least one element from the group consisting of Fe,         Co, Mg, Zn, Cu and mixtures thereof,     -   M2 denotes at least one element from the group consisting of Mn,         Al, B, Ca, Cr and mixtures thereof,     -   b≦0.8     -   c≦0.5     -   d≦0.5, and     -   x is a number between 0.1 and 0.8,     -   y is a number between 1.2 and 1.9, and x+y=2.

Advantageous compounds are chemical compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y), wherein

0.3≦b≦0.6 0.1≦c≦0.4 0.1≦d≦0.4 and/or x is a number between 0.2 and 0.7 and y is a number between 1.3 and 1.8 and x+y=2. The sum of b, c and d is preferably 1.

Particularly preferred compounds are chemical compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) wherein x is a number between 0.3 and 0.6 and y is a number between 1.4 and 1.7.

Compounds which are part of the invention are listed in the following Tables 1 to 17. Individual compounds are designated by the number of the table, followed by the number of the combination of the variables M1, M2, b and c as in Table 1. For example, compound 14.022 is the compound as described in Table 14, wherein the variable x defined there is combined with the combination of variables M1, M2, b and c as in Table 1, position no. 022. In Tables 1 to 17, the compounds have the general formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y), where y=2−x and d=1−b−c.

TABLE 1 No. M1 M2 b c 001 Co Mn 0.333 0.05 002 Co Mn 0.375 0.05 003 Co Mn 0.475 0.05 004 Co Mn 0.5 0.05 005 Co Mn 0.55 0.05 006 Co Mn 0.65 0.05 007 Co Mn 0.7 0.05 008 Co Mn 0.75 0.05 009 Co Mn 0.77 0.05 010 Co Mn 0.333 0.13 011 Co Mn 0.375 0.13 012 Co Mn 0.475 0.13 013 Co Mn 0.5 0.13 014 Co Mn 0.55 0.13 015 Co Mn 0.65 0.13 016 Co Mn 0.7 0.13 017 Co Mn 0.75 0.13 018 Co Mn 0.77 0.13 019 Co Mn 0.333 0.15 020 Co Mn 0.375 0.15 021 Co Mn 0.475 0.15 022 Co Mn 0.5 0.15 023 Co Mn 0.55 0.15 024 Co Mn 0.65 0.15 025 Co Mn 0.7 0.15 026 Co Mn 0.75 0.15 027 Co Mn 0.77 0.15 028 Co Mn 0.333 0.20 029 Co Mn 0.375 0.20 030 Co Mn 0.475 0.20 031 Co Mn 0.5 0.20 032 Co Mn 0.55 0.20 033 Co Mn 0.65 0.20 034 Co Mn 0.7 0.20 035 Co Mn 0.75 0.20 036 Co Mn 0.77 0.20 037 Co Mn 0.333 0.25 038 Co Mn 0.375 0.25 039 Co Mn 0.475 0.25 040 Co Mn 0.5 0.25 041 Co Mn 0.55 0.25 042 Co Mn 0.65 0.25 043 Co Mn 0.7 0.25 044 Co Mn 0.75 0.25 045 Co Mn 0.77 0.23 046 Co Mn 0.333 0.333 047 Co Mn 0.375 0.333 048 Co Mn 0.475 0.333 049 Co Mn 0.5 0.333 050 Co Mn 0.55 0.333 051 Co Mn 0.65 0.333 052 Co Mn 0.7 0.10 053 Co Mn 0.75 0.10 054 Co Mn 0.77 0.10 055 Co Cr 0.333 0.05 056 Co Cr 0.375 0.05 057 Co Cr 0.475 0.05 058 Co Cr 0.5 0.05 059 Co Cr 0.55 0.05 060 Co Cr 0.65 0.05 061 Co Cr 0.7 0.05 062 Co Cr 0.75 0.05 063 Co Cr 0.77 0.05 064 Co Cr 0.333 0.13 065 Co Cr 0.375 0.13 066 Co Cr 0.475 0.13 067 Co Cr 0.5 0.13 068 Co Cr 0.55 0.13 069 Co Cr 0.65 0.13 070 Co Cr 0.7 0.13 071 Co Cr 0.75 0.13 072 Co Cr 0.77 0.13 073 Co Cr 0.333 0.15 074 Co Cr 0.375 0.15 075 Co Cr 0.475 0.15 076 Co Cr 0.5 0.15 077 Co Cr 0.55 0.15 078 Co Cr 0.65 0.15 079 Co Cr 0.7 0.15 080 Co Cr 0.75 0.15 081 Co Cr 0.77 0.15 082 Co Cr 0.333 0.20 083 Co Cr 0.375 0.20 084 Co Cr 0.475 0.20 085 Co Cr 0.5 0.20 086 Co Cr 0.55 0.20 087 Co Cr 0.65 0.20 088 Co Cr 0.7 0.20 089 Co Cr 0.75 0.20 090 Co Cr 0.77 0.20 091 Co Cr 0.333 0.25 092 Co Cr 0.375 0.25 093 Co Cr 0.475 0.25 094 Co Cr 0.5 0.25 095 Co Cr 0.55 0.25 096 Co Cr 0.65 0.25 097 Co Cr 0.7 0.25 098 Co Cr 0.75 0.25 099 Co Cr 0.77 0.23 100 Co Cr 0.333 0.333 101 Co Cr 0.375 0.333 102 Co Cr 0.475 0.333 103 Co Cr 0.5 0.333 104 Co Cr 0.55 0.333 105 Co Cr 0.65 0.333 106 Co Cr 0.7 0.10 107 Co Cr 0.75 0.10 108 Co Cr 0.77 0.10 109 Mg Mn 0.333 0.05 110 Mg Mn 0.375 0.05 111 Mg Mn 0.475 0.05 112 Mg Mn 0.5 0.05 113 Mg Mn 0.55 0.05 114 Mg Mn 0.65 0.05 115 Mg Mn 0.7 0.05 116 Mg Mn 0.75 0.05 117 Mg Mn 0.77 0.05 118 Mg Mn 0.333 0.13 119 Mg Mn 0.375 0.13 120 Mg Mn 0.475 0.13 121 Mg Mn 0.5 0.13 122 Mg Mn 0.55 0.13 123 Mg Mn 0.65 0.13 124 Mg Mn 0.7 0.13 125 Mg Mn 0.75 0.13 126 Mg Mn 0.77 0.13 127 Mg Mn 0.333 0.15 128 Mg Mn 0.375 0.15 129 Mg Mn 0.475 0.15 130 Mg Mn 0.5 0.15 131 Mg Mn 0.55 0.15 132 Mg Mn 0.65 0.15 133 Mg Mn 0.7 0.15 134 Mg Mn 0.75 0.15 135 Mg Mn 0.77 0.15 136 Mg Mn 0.333 0.20 137 Mg Mn 0.375 0.20 138 Mg Mn 0.475 0.20 139 Mg Mn 0.5 0.20 140 Mg Mn 0.55 0.20 141 Mg Mn 0.65 0.20 142 Mg Mn 0.7 0.20 143 Mg Mn 0.75 0.20 144 Mg Mn 0.77 0.20 145 Mg Mn 0.333 0.25 146 Mg Mn 0.375 0.25 147 Mg Mn 0.475 0.25 148 Mg Mn 0.5 0.25 149 Mg Mn 0.55 0.25 150 Mg Mn 0.65 0.25 151 Mg Mn 0.7 0.25 152 Mg Mn 0.75 0.25 153 Mg Mn 0.77 0.23 154 Mg Mn 0.333 0.333 155 Mg Mn 0.375 0.333 156 Mg Mn 0.475 0.333 157 Mg Mn 0.5 0.333 158 Mg Mn 0.55 0.333 159 Mg Mn 0.65 0.333 160 Mg Mn 0.7 0.10 161 Mg Mn 0.75 0.10 162 Mg Mn 0.77 0.10 163 Mg Cr 0.333 0.05 164 Mg Cr 0.375 0.05 165 Mg Cr 0.475 0.05 166 Mg Cr 0.5 0.05 167 Mg Cr 0.55 0.05 168 Mg Cr 0.65 0.05 169 Mg Cr 0.7 0.05 170 Mg Cr 0.75 0.05 171 Mg Cr 0.77 0.05 172 Mg Cr 0.333 0.13 173 Mg Cr 0.375 0.13 174 Mg Cr 0.475 0.13 175 Mg Cr 0.5 0.13 176 Mg Cr 0.55 0.13 177 Mg Cr 0.65 0.13 178 Mg Cr 0.7 0.13 179 Mg Cr 0.75 0.13 180 Mg Cr 0.77 0.13 181 Mg Cr 0.333 0.15 182 Mg Cr 0.375 0.15 183 Mg Cr 0.475 0.15 184 Mg Cr 0.5 0.15 185 Mg Cr 0.55 0.15 186 Mg Cr 0.65 0.15 187 Mg Cr 0.7 0.15 188 Mg Cr 0.75 0.15 189 Mg Cr 0.77 0.15 190 Mg Cr 0.333 0.20 191 Mg Cr 0.375 0.20 192 Mg Cr 0.475 0.20 193 Mg Cr 0.5 0.20 194 Mg Cr 0.55 0.20 195 Mg Cr 0.65 0.20 196 Mg Cr 0.7 0.20 197 Mg Cr 0.75 0.20 198 Mg Cr 0.77 0.20 199 Mg Cr 0.333 0.25 200 Mg Cr 0.375 0.25 201 Mg Cr 0.475 0.25 202 Mg Cr 0.5 0.25 203 Mg Cr 0.55 0.25 204 Mg Cr 0.65 0.25 205 Mg Cr 0.7 0.25 206 Mg Cr 0.75 0.25 207 Mg Cr 0.77 0.23 208 Mg Cr 0.333 0.333 209 Mg Cr 0.375 0.333 210 Mg Cr 0.475 0.333 211 Mg Cr 0.5 0.333 212 Mg Cr 0.55 0.333 213 Mg Cr 0.65 0.333 214 Mg Cr 0.7 0.10 215 Mg Cr 0.75 0.10 216 Mg Cr 0.77 0.10 217 Zn Mn 0.333 0.05 218 Zn Mn 0.375 0.05 219 Zn Mn 0.475 0.05 220 Zn Mn 0.5 0.05 221 Zn Mn 0.55 0.05 222 Zn Mn 0.65 0.05 223 Zn Mn 0.7 0.05 224 Zn Mn 0.75 0.05 225 Zn Mn 0.77 0.05 226 Zn Mn 0.333 0.13 227 Zn Mn 0.375 0.13 228 Zn Mn 0.475 0.13 229 Zn Mn 0.5 0.13 230 Zn Mn 0.55 0.13 231 Zn Mn 0.65 0.13 232 Zn Mn 0.7 0.13 233 Zn Mn 0.75 0.13 234 Zn Mn 0.77 0.13 235 Zn Mn 0.333 0.15 236 Zn Mn 0.375 0.15 237 Zn Mn 0.475 0.15 238 Zn Mn 0.5 0.15 239 Zn Mn 0.55 0.15 240 Zn Mn 0.65 0.15 241 Zn Mn 0.7 0.15 242 Zn Mn 0.75 0.15 243 Zn Mn 0.77 0.15 244 Zn Mn 0.333 0.20 245 Zn Mn 0.375 0.20 246 Zn Mn 0.475 0.20 247 Zn Mn 0.5 0.20 248 Zn Mn 0.55 0.20 249 Zn Mn 0.65 0.20 250 Zn Mn 0.7 0.20 251 Zn Mn 0.75 0.20 252 Zn Mn 0.77 0.20 253 Zn Mn 0.333 0.25 254 Zn Mn 0.375 0.25 255 Zn Mn 0.475 0.25 256 Zn Mn 0.5 0.25 257 Zn Mn 0.55 0.25 258 Zn Mn 0.65 0.25 259 Zn Mn 0.7 0.25 260 Zn Mn 0.75 0.25 261 Zn Mn 0.77 0.23 262 Zn Mn 0.333 0.333 263 Zn Mn 0.375 0.333 264 Zn Mn 0.475 0.333 265 Zn Mn 0.5 0.333 266 Zn Mn 0.55 0.333 267 Zn Mn 0.65 0.333 268 Zn Mn 0.7 0.10 269 Zn Mn 0.75 0.10 270 Zn Mn 0.77 0.10 271 Zn Cr 0.333 0.05 272 Zn Cr 0.375 0.05 273 Zn Cr 0.475 0.05 274 Zn Cr 0.5 0.05 275 Zn Cr 0.55 0.05 276 Zn Cr 0.65 0.05 277 Zn Cr 0.7 0.05 278 Zn Cr 0.75 0.05 279 Zn Cr 0.77 0.05 280 Zn Cr 0.333 0.13 281 Zn Cr 0.375 0.13 282 Zn Cr 0.475 0.13 283 Zn Cr 0.5 0.13 284 Zn Cr 0.55 0.13 285 Zn Cr 0.65 0.13 286 Zn Cr 0.7 0.13 287 Zn Cr 0.75 0.13 288 Zn Cr 0.77 0.13 289 Zn Cr 0.333 0.15 290 Zn Cr 0.375 0.15 291 Zn Cr 0.475 0.15 292 Zn Cr 0.5 0.15 293 Zn Cr 0.55 0.15 294 Zn Cr 0.65 0.15 295 Zn Cr 0.7 0.15 296 Zn Cr 0.75 0.15 297 Zn Cr 0.77 0.15 298 Zn Cr 0.333 0.20 299 Zn Cr 0.375 0.20 300 Zn Cr 0.475 0.20 301 Zn Cr 0.5 0.20 302 Zn Cr 0.55 0.20 303 Zn Cr 0.65 0.20 304 Zn Cr 0.7 0.20 305 Zn Cr 0.75 0.20 306 Zn Cr 0.77 0.20 307 Zn Cr 0.333 0.25 308 Zn Cr 0.375 0.25 309 Zn Cr 0.475 0.25 310 Zn Cr 0.5 0.25 311 Zn Cr 0.55 0.25 312 Zn Cr 0.65 0.25 313 Zn Cr 0.7 0.25 314 Zn Cr 0.75 0.25 315 Zn Cr 0.77 0.23 316 Zn Cr 0.333 0.333 317 Zn Cr 0.375 0.333 318 Zn Cr 0.475 0.333 319 Zn Cr 0.5 0.333 320 Zn Cr 0.55 0.333 321 Zn Cr 0.65 0.333 322 Zn Cr 0.7 0.10 323 Zn Cr 0.75 0.10 324 Zn Cr 0.77 0.10 325 Cu Mn 0.333 0.05 326 Cu Mn 0.375 0.05 327 Cu Mn 0.475 0.05 328 Cu Mn 0.5 0.05 329 Cu Mn 0.55 0.05 330 Cu Mn 0.65 0.05 331 Cu Mn 0.7 0.05 332 Cu Mn 0.75 0.05 333 Cu Mn 0.77 0.05 334 Cu Mn 0.333 0.13 335 Cu Mn 0.375 0.13 336 Cu Mn 0.475 0.13 337 Cu Mn 0.5 0.13 338 Cu Mn 0.55 0.13 339 Cu Mn 0.65 0.13 340 Cu Mn 0.7 0.13 341 Cu Mn 0.75 0.13 342 Cu Mn 0.77 0.13 343 Cu Mn 0.333 0.15 344 Cu Mn 0.375 0.15 345 Cu Mn 0.475 0.15 346 Cu Mn 0.5 0.15 347 Cu Mn 0.55 0.15 348 Cu Mn 0.65 0.15 349 Cu Mn 0.7 0.15 350 Cu Mn 0.75 0.15 351 Cu Mn 0.77 0.15 352 Cu Mn 0.333 0.20 353 Cu Mn 0.375 0.20 354 Cu Mn 0.475 0.20 355 Cu Mn 0.5 0.20 356 Cu Mn 0.55 0.20 357 Cu Mn 0.65 0.20 358 Cu Mn 0.7 0.20 359 Cu Mn 0.75 0.20 360 Cu Mn 0.77 0.20 361 Cu Mn 0.333 0.25 362 Cu Mn 0.375 0.25 363 Cu Mn 0.475 0.25 364 Cu Mn 0.5 0.25 365 Cu Mn 0.55 0.25 366 Cu Mn 0.65 0.25 367 Cu Mn 0.7 0.25 368 Cu Mn 0.75 0.25 369 Cu Mn 0.77 0.23 370 Cu Mn 0.333 0.333 371 Cu Mn 0.375 0.333 372 Cu Mn 0.475 0.333 373 Cu Mn 0.5 0.333 374 Cu Mn 0.55 0.333 375 Cu Mn 0.65 0.333 376 Cu Mn 0.7 0.10 377 Cu Mn 0.75 0.10 378 Cu Mn 0.77 0.10 379 Cu Cr 0.333 0.05 380 Cu Cr 0.375 0.05 381 Cu Cr 0.475 0.05 382 Cu Cr 0.5 0.05 383 Cu Cr 0.55 0.05 384 Cu Cr 0.65 0.05 385 Cu Cr 0.7 0.05 386 Cu Cr 0.75 0.05 387 Cu Cr 0.77 0.05 388 Cu Cr 0.333 0.13 389 Cu Cr 0.375 0.13 390 Cu Cr 0.475 0.13 391 Cu Cr 0.5 0.13 392 Cu Cr 0.55 0.13 393 Cu Cr 0.65 0.13 394 Cu Cr 0.7 0.13 395 Cu Cr 0.75 0.13 396 Cu Cr 0.77 0.13 397 Cu Cr 0.333 0.15 398 Cu Cr 0.375 0.15 399 Cu Cr 0.475 0.15 400 Cu Cr 0.5 0.15 401 Cu Cr 0.55 0.15 402 Cu Cr 0.65 0.15 403 Cu Cr 0.7 0.15 404 Cu Cr 0.75 0.15 405 Cu Cr 0.77 0.15 406 Cu Cr 0.333 0.20 407 Cu Cr 0.375 0.20 408 Cu Cr 0.475 0.20 409 Cu Cr 0.5 0.20 410 Cu Cr 0.55 0.20 411 Cu Cr 0.65 0.20 412 Cu Cr 0.7 0.20 413 Cu Cr 0.75 0.20 414 Cu Cr 0.77 0.20 415 Cu Cr 0.333 0.25 416 Cu Cr 0.375 0.25 417 Cu Cr 0.475 0.25 418 Cu Cr 0.5 0.25 419 Cu Cr 0.55 0.25 420 Cu Cr 0.65 0.25 421 Cu Cr 0.7 0.25 422 Cu Cr 0.75 0.25 423 Cu Cr 0.77 0.23 424 Cu Cr 0.333 0.333 425 Cu Cr 0.375 0.333 426 Cu Cr 0.475 0.333 427 Cu Cr 0.5 0.333 428 Cu Cr 0.55 0.333 429 Cu Cr 0.65 0.333 430 Cu Cr 0.7 0.10 431 Cu Cr 0.75 0.10 432 Cu Cr 0.77 0.10

Table 2:

Table 2 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.13, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 3:

Table 3 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.15, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 4:

Table 4 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.17, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 5:

Table 5 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.21, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 6:

Table 6 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.22, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 7:

Table 7 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.23, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 8:

Table 8 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.26, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 9:

Table 9 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.28, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 10:

Table 10 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.30, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 11:

Table 11 consists of 432 compounds of the formula) Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.37, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 12:

Table 12 consists of 432 compounds of the formula) Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.4, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 13:

Table 13 consists of 432 compounds of the formula) Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.42, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 14:

Table 14 consists of 432 compounds of the formula) Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.48, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 15:

Table 15 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.5, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 16:

Table 16 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.6, wherein the values of the variables M1, M2, b and c are listed in Table 1.

Table 17:

Table 17 consists of 432 compounds of the formula Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) where y=2−x and d=1−b−c and x=0.69, wherein the values of the variables M1, M2, b and c are listed in Table 1.

The chemical compounds according to the invention are partly oxidized mixed metal hydroxides, later also called precursor(s).

The parameters x and y stated in the partly oxidized mixed metal hydroxides according to the invention unambiguously define the average degree of oxidation over all the metallic components of the mixed metal hydroxide. It has now been found that the partly oxidized mixed metal hydroxides having an average degree of oxidation of from 2.1 to 2.8 can be processed particularly readily to end products of the general formula Li_(a)Ni_(b)M1_(c)M2_(d)(O)₂ wherein M1 denotes at least one element chosen from the group consisting of Fe, Co, Mg, Zn, Cu and mixtures thereof and/or M2 denotes at least one element of the group consisting of Mn, Al, B, Ca, Cr, the index a is 0.95≦=a≦=1.15, in particular a is 0.98≦=a≦=1.10, the indices b, c and d are defined above, which have a considerably better cycle stability, improved charging/ischarging properties in the lithium secondary batteries and a higher tap density and particularly good sieving properties. These compounds of the general formula Li_(a)Ni_(b)M1_(c)M2_(d)(O)₂ are also called end product in the following.

The average degree of oxidation is also an indicator for evaluation of the quality of the precursor for lithium secondary batteries. Precise adjustment of this parameter during the preparation process is therefore necessary.

It has been found, surprisingly, that the average degree of oxidation of the partly oxidized mixed metal hydroxide according to the invention should not be below a certain level in order to ensure good further processability and finally a good quality of the end product. It has also been found that the average degree of oxidation should not be too high, since a secondary phase, such as a gamma-oxyhydroxide, may increasingly occur in the precursor at degrees of oxidation which are too high. The presence of the gamma phase alongside the desired beta phase means an inhomogeneity of the precursor and finally also influences the homogeneity of the end product obtainable therefrom. Due to the interlaminar extension of the crystal lattice compared with the beta phase, the existence of a gamma phase furthermore promotes the undesirable inclusion of ionic impurities.

Preferably, the average degree of oxidation is 2.2 to 2.7, particularly preferably 2.3 to 2.6.

The determination of the average degree of oxidation over all the metallic components is based on the Rupp method of manganese dioxide determination.

The degree of oxidation determined by means of the method mentioned is the basis for evaluation of the empirical formula of the present chemical compound.

The following quantitative relationship exists between the index x and the degree of oxidation α:

α=x+2

This means e.g. that in the case of an average oxidation level over all the metals of +2.5, a value of (2.5−2)=0.5 results for the index x, which leads to an empirical formula such as, for example,

NiCoMn(O)_(0.5)(OH)_(1.5).

The partly oxidized mixed metal hydroxides according to the invention are distinguished in particular in that these contain no gamma-oxyhydroxide structures. FIG. 1 shows by way of example an x-ray diffraction spectrum (XDS) of a partly oxidized mixed metal hydroxide according to the invention, which was prepared according to Example 1 and in which no gamma phase is detectable.

Preferred partly oxidized mixed metal hydroxides according to the invention contain no alpha phase.

The presence of the alpha phase alongside the desired beta phase means an inhomogeneity of the precursor and finally also influences the homogeneity of the end product obtainable therefrom.

It was furthermore to be found that as the degree of oxidation increases, e.g. when the latter reaches a value of e.g. 3.0 in the oxidized mixed metal hydroxide, the ionic impurities, those such as e.g. sodium, in the product increase, since in the phase conversion to the gamma-oxyhydroxide greater distances between layers in the crystal lattice render possible the incorporation of undesirable foreign ions. The gamma phase leads to a considerable expansion in volume due to an interlaminar extension and thereby promotes the embedding of foreign ions.

The partly oxidized mixed metal hydroxides according to the invention are also distinguished in that they have low sodium contents. Preferably, they contain <2,000 ppm, particularly preferably <1,000 ppm of sodium, in particular <500 ppm of sodium.

The partly oxidized mixed metal hydroxides according to the invention are preferably in powder form, the average particle size of the secondary particles, measured in accordance with ASTM B822, preferably being 2 to 30 μm, particularly preferably 3 to 15 μm. Secondary particles are understood as meaning particles which are composed of primary particles.

A particular feature of the mixed metal hydroxide powder according to the invention is its high tap density, which has a direct influence directly on the tap density of the end product, e.g. a lithium mixed metal oxide. The high tap density is necessary in order to achieve a high volumetric energy density in the battery. Preferably, the partly oxidized mixed metal hydroxide powders according to the invention have a tap density, determined in accordance with ASTM B527, of greater than 1.7 g/cm³, particularly preferably greater than 1.9 g/cm³.

The pulverulent mixed metal hydroxides according to the invention can be prepared both in a spherical and in a regular (non-spherical) particle shape.

The preferred powders according to the invention are distinguished in particular by the spherical shape of the powder particles, the shape factor of which has a value of greater than 0.7, particularly preferably of greater than 0.9.

The shape factor of the secondary particles can be determined by the method mentioned in U.S. Pat. No. 5,476,530, columns 7 and 8 and FIG. 5. This method determines a shape factor of the particles which is a measure of the sphericity of the particles. The shape factor of the particles can be determined from the SEM photographs of the materials.

The shape factor is determined by evaluation of the particle circumference and the particle area and of the determination of the diameter deduced from the particular parameters. The diameters mentioned result from

d _(U) =U/Π d _(A)=(4A/Π)^(1/2).

The shape factor of the particles f is deduced from the particle circumference U and the particle area A according to:

${f = {\left( \frac{d_{A}}{d_{U}} \right) = \left( \frac{4\; \pi \; A}{U^{2}} \right)}},$

In the case of an ideal spherical particle, d_(A) and d_(U) are equal and a shape factor of precisely one would result.

FIG. 2 shows by way of example a photograph of the partly oxidized mixed metal hydroxide powder according to the invention prepared according to Example 1 taken with a scanning electron microscope (SEM).

The partly oxidized mixed metal hydroxide powders according to the invention have a standardized width of the particle size distribution, defined according to the formula

$\frac{{D\; 90} - {D\; 10}}{D\; 50}$

wherein D denotes the diameter of the powder particles, of less than 1.8, particularly preferably of less than 1.2.

The invention furthermore relates to an efficient and economical process for the preparation of the partly oxidized mixed metal hydroxides according to the invention.

The invention therefore also provides a process for the preparation of the partly oxidized mixed metal hydroxides according to the invention comprising the following steps:

-   -   co-precipitation of spherical mixed metal hydroxides from         corresponding metal salt solutions,     -   partial oxidation of the precipitation product (mixed metal         hydroxide) using an oxidizing agent,     -   separating off of the co-precipitated partly oxidized mixed         metal hydroxide from the suspension,     -   washing and drying of the partly oxidized mixed metal hydroxide

The partly oxidized mixed metal hydroxides according to the invention can be prepared both in a spherical and in a non-spherical particle shape, the preparation of the former being carried out in the presence of ammonia or ammonium salts.

Mixed hydroxides are prepared by precipitation from aqueous metal salt solutions by adjusting the pH to 8-14, particularly preferably to 9-13, by addition of alkali hydroxide solutions. The process can be carried out discontinuously or continuously. In the continuous process, metal salt solution and the alkali hydroxide solution are added simultaneously to a precipitating reactor, with continuous removal of the product suspension. Suitable metal salts are water-soluble metal salts, e.g. sulfates, nitrates, halides, such as e.g. chlorides or fluorides. Alkali metal salt solutions which are employed for carrying out the precipitation are hydroxides of the alkali metals, preferably sodium hydroxide, as well as ammonium hydroxide.

An oxidation of the metals should be avoided during the precipitation process, in order to be able to achieve a high tap density of the partly oxidized mixed metal hydroxide. The oxidation is therefore carried out after the precipitation in a further reactor.

In order to be able to synthesize the partly oxidized mixed metal hydroxides according to the invention with an increased degree of oxidation on a commercial scale, the invention provides a process which is particularly suitable in respect of simple ease of integration into the existing production process. In this process, the partial oxidation of the co-precipitated mixed metal hydroxide can still take place in the product suspension. The process is realized by transferring the product suspension with the co-precipitated mixed metal hydroxide from the precipitating reactor into a subsequent stirred tank. An oxidizing agent is fed into this tank via an inlet tube. Air, oxygen, hydrogen peroxide, sodium peroxydisulfate, potassium peroxydisulfate and/or mixtures thereof are particularly suitable oxidizing agents.

Preferably, the reaction temperature of the suspension during the partial oxidation is 25 to 65° C., particularly preferably 30 to 60° C.

The pH of the suspension during the partial oxidation of the mixed metal hydroxide is preferably 7-13, particularly preferably 8-12.

The dwell time of the product suspension in the reaction tank likewise plays an important role during the partial oxidation. It has now been found that the dwell time of from 1 to 10 hours, preferably of from 2 to 8 hours and particularly preferably of from 4 to 6 hours leads to partly oxidized mixed metal hydroxides according to the invention.

After the oxidation step, the partly oxidized mixed metal hydroxide is removed continuously. However, it is also possible to remove the product in portions. The partly oxidized mixed metal hydroxide according to the invention is then washed on a suction filter and dried in a drying cabinet.

The preparation of partly oxidized mixed metal hydroxides according to the invention can also be carried out via another process by separating off the co-precipitated mixed metal hydroxides from the suspension, washing them and drying them under an oxygen-containing atmosphere, such as e.g. air.

The invention therefore provides a further process comprising the following steps:

-   -   co-precipitation of spherical mixed metal hydroxides from         corresponding metal salt solutions,     -   separating off of the co-precipitated mixed metal hydroxide from         the suspension,     -   washing of the mixed metal hydroxide,     -   drying and simultaneous partial oxidation of the mixed metal         hydroxide under an oxygen-containing atmosphere at a temperature         of greater than 80° C. for at least 3 hours.

The partly oxidized mixed metal hydroxides according to the invention are particularly suitable for the synthesis of end products having the chemical formula Li_(a)Ni_(b)M1_(c)M2_(d)(O)₂, also called end product, which are employed as the active material for positive electrodes in secondary batteries. The partly oxidized mixed metal hydroxides according to the invention are conceived such that the end product obtainable therefrom—lithium mixed metal oxide—can be prepared via a simple synthesis route.

The invention furthermore provides a process for the preparation of active materials for secondary batteries comprising the following steps:

-   -   mixing of a chemical compound according to one of claims 1 to 18         with a lithium-containing component,     -   calcining and sieving of the mixture.

In this process, the chemical reaction of the precursor proceeds to a chemical compound Li_(a)Ni_(b)M1_(c)M2_(d)(O)₂, wherein M1 is at least one element chosen from the group consisting of Fe, Co, Mg, Zn, Cu and mixtures thereof and/or M2 is at least one element chosen from the group consisting of Mn, Al, B, Ca, Cr and mixtures thereof, the particle shape and/or particle size distribution being retained.

The end product can be prepared by mixing the partly oxidized mixed metal hydroxide according to the invention with a lithium-containing component and then calcining and sieving the mixture. Suitable lithium-containing components are, in particular, lithium hydroxide, lithium carbonate, lithium nitrate and/or mixtures thereof. The calcining can be carried out at temperatures of greater than 600° C., preferably of greater than 700° C.

The end product obtainable from the partly oxidized mixed metal hydroxide according to the invention is distinguished in particular by very good sieving properties. The sieving yield of the end product is greater than 90%, preferably greater than 95%, particularly preferably greater than 98%.

The partly oxidized mixed metal hydroxides according to the invention are preferably employed as a precursor for cathode active material in lithium secondary batteries, together with materials known to the person skilled in the art.

The invention is explained in more detail with the aid of the following examples.

The average degrees of oxidation stated in the following examples are determined by the Rupp method. This method is based on the method of determination of manganese dioxide. In this, metal ions of higher valency (valency +3 or +4 in this case) are reduced to metal(II) ions by iodide, the iodide being oxidized to elemental iodine. The iodine formed is determined by means of titration against sodium thiosulfate standard solution. The equivalent point is indicated with starch solution.

0.2 g of the test material is weighed into a 500 ml conical flask with a ground glass joint on an analytical balance. 50 ml of potassium iodide solution and 25 ml of dilute sulfuric acid are added by means of a 50 ml measuring cylinder. The conical flask is then closed with a glass stopper.

The test material is dissolved at room temperature by occasional swirling of the conical flask. The dissolving time is 30 to 60 min.

When the sample has dissolved completely, titration is carried out against sodium thiosulfate standard solution with addition of approx. 5 drops of starch solution, until the colour changes detectably from brown/blue to pale green.

To determine any interfering reactions, it is necessary to run a blank sample in parallel in the analysis operation. The consumption of sodium thiosulfate standard solution is to be included in the evaluation.

The average degree of oxidation over all the metals of the compound can be calculated via the following formula:

$\alpha = {2 + \frac{\begin{matrix} {\left( {{V\left( {{Na}_{2}S_{2}O_{3,{sample}}} \right)} - {V\left( {{Na}_{2}S_{2}O_{3,{blank}}} \right)}} \right) \cdot} \\ {{{titre}\left( {{Na}_{2}S_{2}O_{3}} \right)} \cdot {c\left( {{Na}_{2}S_{2}O_{3}} \right)} \cdot {M({sample})}} \end{matrix}}{m({sample})}}$

EXAMPLES Example 1

A solution which is in each case 0.7 molar in NiSO₄, CoSO₄ and MnSO₄ is fed continuously to a precipitating reactor. In addition to the metal-containing solutions, a 2.5 molar NaOH solution and a 12.5% strong NH₃ solution are simultaneously fed continuously into the reactor. These streams are metered such that an ammonia concentration of 30 g/l and a free sodium hydroxide solution concentration of 1.4 g/l are established in the stationary operating state. Under these conditions, a pH of 12.4 is established. The high pH ensures that the metallic components are precipitated as hydroxides from the metal-containing solutions. The addition of the various feed solutions results in a solids concentration in the reactor of 40 g/l. The temperature in the reactor is regulated to 50° C. by means of an external supply of heat. The average dwell time of the solid in the reactor is 6 h.

The product suspension is removed continuously from the reactor and first fed to washing on a suction filter. Washing is necessary in order to separate the solid from adhering impurities.

After washing of the hydroxide, drying for 24 h and parallel oxidation of the solid are carried out in a circulating air drying cabinet under an oxygen-containing atmosphere at 100° C.

In the compound synthesized, the metals nickel, cobalt and manganese have a molar ratio of Ni:Co:Mn=1:1:1.

The solid synthesized in this way has an average oxidation level over all the metals, determined by experiment, of 2.7.

The tap density of the material was measured as 1.74 g/cm³. The SEM photograph in FIG. 2 shows the particular sphericity and also the pronounced compactness of the particles of the material synthesized in this way.

The shape factor determined for the material is 0.85.

For further conversion of the precursor into the end product, the precursor was first mixed mechanically with technical-grade lithium carbonate (Chemetall). The molar ratio of the lithium compound to the precursor in this case was 1.05:1.00.

The mechanical mixture was then calcined at 890° C. under an oxygen-containing atmosphere for 30 hours.

After the calcining, the material was sieved.

The sieving yield was 97.5%. 2.5% of the material could not be sieved through a 50 μm sieve. After the sieving, the material was subjected to a second calcining at 890° C. under an oxygen-containing atmosphere for 4 hours. Thereafter, sieving was carried out again with a sieving yield of 99.6%.

The tap density of the end product here was 2.0 g/cm³.

It can be seen from the SEM photographs of the end product, FIGS. 3 and 4, that the conversion of the precursor into the end product has taken place with retention of the spherical shape of the secondary particles of the precursor.

Comparison Example 1

A solution which is in each case 0.7 molar in NiSO₄, CoSO₄ and MnSO₄ is fed continuously to a precipitating reactor. In addition to the metal-containing solutions, a 2.5 molar NaOH solution and a 12.5% strong NH₃ solution are simultaneously fed continuously into the reactor. These streams are metered such that an ammonia concentration of 8.3 g/l and a free sodium hydroxide solution concentration of 0.5 g/l are established in the stationary operating state. Under these conditions, a pH of 12.0 is established. The high pH ensures that the metallic components are precipitated as hydroxides from the metal-containing solutions. The addition of the various feed solutions results in a solids concentration in the reactor of 80 g/l. The temperature in the reactor is regulated to 45° C. by means of an external supply of heat. The average dwell time of the solid in the reactor is 12 h.

The product suspension is removed continuously from the reactor and first fed to a filtration and washing. Washing is necessary in order to separate the solid from adhering impurities.

After washing of the hydroxide, the solid was dried at 70° C.

In the compound synthesized, the metals nickel, cobalt and manganese have a molar ratio of Ni:Co:Mn=1:1:1. The mixed hydroxide synthesized in this way had an average oxidation level over all the metals, determined by experiment, of 2.07.

The x-ray diffraction spectrum for the compound synthesized is shown in FIG. 5.

For further conversion of the precursor into the end product, the precursor was first mixed mechanically with technical-grade lithium carbonate (Chemetall). The molar ratio of the lithium compound to the mixed metal compound in this case was 1.07:1.00.

The mechanical mixture was then calcined at 860° C. under an oxygen-containing atmosphere for 30 hours.

After the calcining, the material was sieved. The sieving yield was 64%.

It can be seen from the SEM photographs of the end product, FIGS. 6 and 7, that during the conversion of the precursor into the end product the spherical particle shape of the precursor is lost due to the irregular growth of the primary particles.

A comparison of the electrochemical performance data of half cells which comprise the material synthesized according to Example 1 and that according to Comparison Example 1 as the cathode active material is shown in FIG. 8. It can be seen from the figure that a half cell produced with the substance from Example 1 shows better performance data compared with a half cell produced with the substance from Comparison Example 1.

Example 2

A solution which is in each case 0.7 molar in NiSO₄, CoSO₄ and MnSO₄ is fed continuously to a precipitating reactor. A 2.5 molar NaOH solution and a 12.5% strong NH₃ solution are simultaneously fed continuously into the reactor. These streams are metered such that an ammonia concentration of 8 g/l and a free sodium hydroxide solution concentration of 0.5 g/l are established in the stationary operating state. Under these conditions, a pH of 12.0 is established. The high pH ensures that the metallic components are precipitated as hydroxides from the metal-containing solutions. The addition of the various feed solutions results in a solids concentration in the reactor of 50 g/l. The temperature in the reactor is regulated to 50° C. by means of an external supply of heat. The average dwell time of the solid in the reactor is 5 h.

The product suspension is fed continuously from the precipitating reactor to a second reactor, in which the pH is adjusted to 12.0 by means of pH control and metering in of 2.5 molar NaOH solution and the temperature is adjusted to 50° C. by means of an external supply of heat. The average dwell time is adjusted to 10 h. Air is introduced into this second reactor with a volume flow of 0.5 litre/min. During this procedure, the suspension changes its colour from pale brown in the first reactor to dark brown to black in the second reactor. The suspension is removed continuously from the second reactor, and initially fed to washing on a suction filter. Washing is necessary in order to separate the solid from adhering impurities. After washing of the product, the solid is dried for 24 h in a vacuum drying cabinet at 100° C.

In the compound synthesized, the metals nickel, cobalt and manganese have a molar ratio of Ni:Co:Mn=1:1:1.

The solid synthesized in this way has an average oxidation level over all the metals, determined by experiment, of 2.39. The sodium content of the product is 70 ppm. In the XDA spectrum, FIG. 9, only peaks which can be assigned to a β structure are detected. No further phases are to be found in the XDA spectrum.

Comparison Example 2

A solution which is in each case 0.7 molar in NiSO₄, CoSO₄ and MnSO₄ is fed continuously to a precipitating reactor. A 2.5 molar NaOH solution and a 12.5% strong NH₃ solution are simultaneously fed continuously into the reactor. These streams are metered such that an ammonia concentration of 8 g/l and a free sodium hydroxide solution concentration of 0.5 g/l are established in the stationary operating state. Under these conditions, a pH of 12.0 is established. The high pH ensures that the metallic components are precipitated as hydroxides from the metal-containing solutions. The addition of the various feed solutions results in a solids concentration in the reactor of 50 g/l. The temperature in the reactor is regulated to 50° C. by means of an external supply of heat. The average dwell time of the solid in the reactor is 5 h.

The product suspension is fed continuously from the precipitating reactor to a second reactor, in which the pH is adjusted to 12.5 by means of pH control and metering in of 2.5 molar NaOH solution and the temperature is adjusted to 70° C. by means of an external supply of heat. The average dwell time is adjusted to 15 h. Air is introduced into this second reactor with a volume flow of 0.5 litre/min. During this procedure, the suspension changes its colour from pale brown in the first reactor to dark brown to black in the second reactor. The suspension is removed continuously from the second reactor, and initially fed to washing on a suction filter. Washing is necessary in order to separate the solid from adhering impurities. After washing of the product, the solid is dried for 24 h in a vacuum drying cabinet at 100° C.

In the compound synthesized, the metals nickel, cobalt and manganese have a molar ratio of Ni:Co:Mn=1:1:1. The solid synthesized in this way has an average oxidation level over all the metals, determined by experiment, of 2.83. The sodium content of the product is 3,000 ppm. In the XDA spectrum, FIG. 10, contents of a gamma phase are detected, in addition to the peaks, which can be assigned to a beta structure.

Further examples of the partial oxidation of the mixed metal compounds in suspension are shown in the following Table 18:

TABLE 18 Temper- Dwell Degree of pH ature time Oxidizing oxidation — ° C. h agent — 11.5 50 8 air 2.33 12.0 50 8 air 2.37 12.0 60 8 air 2.61 12.5 60 8 air 2.69 12.5 60 5 air 2.43 12.8 60 8 air 2.67 12.5 60 5 oxygen 2.47 12 50 2 H₂O₂ 2.36 12 60 2 H₂O₂ 2.54 

1.-37. (canceled)
 38. A process for producing partly oxidized mixed metal hydroxides having a chemical compound of the formula: Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) wherein M1 denotes at least one element selected from the group consisting of Fe, Co, Mg, Zn, Cu and mixtures thereof, M2 denotes at least one element selected from the group consisting of Mn, Al, B, Ca, Cr and mixtures thereof, b≦0.8 c≦0.5 d≦0.5, and x is a number between 0.1 and 0.8, y is a number between 1.2 and 1.9, and x+y=2, which process comprises the steps of: co-precipitation of spherical mixed metal hydroxides from corresponding metal salt solutions, separating off of the co-precipitated mixed metal hydroxide from the suspension, washing of the mixed metal hydroxide, and drying and simultaneous partial oxidation of the mixed metal hydroxide under an oxygen-containing atmosphere at a temperature of greater than 80° C. for at least 3 hours.
 39. A process for producing partly oxidized mixed metal hydroxides having a chemical compound of the formula: Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) wherein M1 denotes at least one element selected from the group consisting of Fe, Co, Mg, Zn, Cu and mixtures thereof, M2 denotes at least one element from the group consisting of Mn, Al, B, Ca, Cr and mixtures thereof, b≦0.8 c≦0.5 d≦0.5, and x is a number between 0.1 and 0.8, y is a number between 1.2 and 1.9, and x+y=2, which process comprises the steps of: co-precipitation of spherical mixed metal hydroxides from corresponding metal salt solutions, separating off of the co-precipitated mixed metal hydroxide from the suspension, washing of the mixed metal hydroxide, and drying and simultaneous partial oxidation of the mixed metal hydroxide under an oxygen-containing atmosphere at a temperature of greater than 80° C. for at least 3 hours, wherein the average degree of oxidation is 2.1 to 2.8.
 40. A process for producing partly oxidized mixed metal hydroxides having a chemical compound of the formula: Ni_(b)M1_(c)M2_(d)(O)_(x)(OH)_(y) wherein M1 denotes at least one element selected from the group consisting of Fe, Co, Mg, Zn, Cu and mixtures thereof, M2 denotes at least one element from the group consisting of Mn, Al, B, Ca, Cr and mixtures thereof, b≦0.8 c≦0.5 d≦0.5, and x is a number between 0.1 and 0.8, y is a number between 1.2 and 1.9, and x+y=2, which process comprises the steps of: co-precipitation of spherical mixed metal hydroxides from corresponding metal salt solutions, separating off of the co-precipitated mixed metal hydroxide from the suspension, washing of the mixed metal hydroxide, and drying and simultaneous partial oxidation of the mixed metal hydroxide under an oxygen-containing atmosphere at a temperature of greater than 80° C. for at least 3 hours, wherein the sodium content of partly oxidized mixed metal hydroxides is less than 2,000 ppm. 